Quality Properties Of Activated Charcoal Of Bidara Wood (Ziziphus Mauritiana) With The Addition Of 𝐇𝟑𝐏𝐎𝟒 Solution Based On Activation Temperature Variation

Naurah Fadillah Azzahra, Devi Tanggasari

Abstract


One of the materials that can be used to make activated charcoal is bidara wood. Bidara wood has a high carbon content and a good pore structure. In addition, bidara wood also contains several minerals such as calcium, potassium, and magnesium in small amounts. The content of these compounds and elements makes bidara wood very suitable to be used as a raw material for activated charcoal. One of the activation materials is an H3PO4 solution. In the activation process, bidara wood activated charcoal can improve its quality properties, such as surface area, pore volume, and adsorption capacity. Therefore, the aim of this research is to determine the effect of heating temperature variations on the quality properties of bidara wood activated charcoal using chemical activation with an H3PO4 solution. The experimental design used in this study is a Completely Randomized Design with one factor, which is the activation temperature (500, 600, and 700˚C). The results of the study showed that the use of H3PO4 solution at a temperature variation of 700˚C resulted in better properties for moisture content (5.41%), ash content (43.29%), and iodine adsorption capacity (4,737 mg/g) compared to the temperature variations of 500˚C and 600˚C.


Keywords


activated charcoal, charcoal activation, bidara wood

Full Text:

PDF

References


Arang, K., Cabang, A., Duri, B., Ex, B. I., Adawi, T. F., Mahakam, I., Aji, L., & Rini, S. (2021). ( Effect of Temperature and Concentration of Phosphoric Acid ( H 3 PO 4 ) on the Quality of. 5, 62–73.

Aryani, F., & Mardiana, F. (2019). ISSN 2655 4887 ( Print ), ISSN 2655 1624 ( Online ). 1(2), 16–20.

Chairunnisa, S., Wartini, N. M., Suhendra, L., Pertanian, F. T., Udayana, U., & Bukit, K. (2019). Pengaruh Suhu dan Waktu Maserasi terhadap Karakteristik Ekstrak Daun Bidara ( Ziziphus mauritiana L . ) sebagai Sumber Saponin. 7(4), 551–560.

Dewi, R., Dari, C., & Aktif, K. (2020). Jurnal Teknologi Kimia Unimal. 2(Nopember), 12–22.

Dungir, S. G., Katja, D. G., & Kamu, V. S. (2012). Aktivitas Antioksidan Ekstrak Fenolik dari Kulit Buah Manggis ( Garcinia mangostana L .). 1(1), 11–15.

Hendrawan, Y., Sutan, S. M., & R, R. K. Y. (2017). Pengaruh Variasi Suhu Karbonisasi dan Konsentrasi Aktivator terhadap Karakteristik Karbon Aktif dari Ampas Tebu ( Bagasse ) Menggunakan Activating Agent NaCl. 5(3), 200–207.

Mody Lempang, Wasrin Syafii, Gustan Pari. (2012). Sifat dan Mutu Arang Aktif Tempurung Kemiri. Jurnal Penelitian Hasil Hutan, 100-113.

Po, T. H., Hco, K. H. P. O., & Fax, T. (2017). Website : http://ejournal.undip.ac.id/index.php/reaktor/ Produksi Karbon Aktif dari Batubara Bituminus dengan Aktivasi.

Rizaldi, L. H., Nasution, N. M., & Indriani, W. (2023). Initial Characterization of Activated Charcoal from the Indigenous Ziziphus mauritiana Wood from Dryland of Sumbawa. 11(2), 270–280. https://doi.org/10.29303/jrpb.v11i2.536

Rozanna Dewi, Azhari dan Indra Nofriadi . (2020). Aktivasi Karbon Dari Kulit Pinang Dengan Menggunakan Aktivator Kimia Koh . Jurnal Teknologi Kimia Unimal, 12-22.

Selan, A. (2016). Pemanfaatan Kulit Singkong Sebagai Bahan Baku Karbon Aktif. 32–36.

Siahaan, S., Hutapea, M., Hasibuan, R., Kimia, D. T., Teknik, F., & Utara, U. S. (2013). PENENTUAN KONDISI OPTIMUM SUHU DAN WAKTU KARBONISASI. 2(1), 26–30.

So, P. H., Suhu, V., & Waktu, D. A. N. (2014). C selama 120 menit. Pengujian kadar abu dengan menimbang arang aktif sebanyak 1 gram lalu memasukkan pada furnace dengan suhu 500. 31–38.

Siti Jamilatun, Intan Dwi Isparulita, Elza Novita Putri . (2014). Karakteristik Arang Aktif Dari Tempurung Kelapa Dengan Pengaktivasi H2so4 Variasi Suhu Dan Waktu. Simposium Nasional Teknologi Terapan, 31-38.

Turmiya Fathal Adawi, Irwan Mahakam Lesmono Aji, Dwi Sukma Rini. (2021). Pengaruh Suhu Dan Konsentrasi Asam Fosfat (H3po4) Terhadap Kualitas Arang Aktif Cabang Bambu Duri (Bambusa blumeana BI. Ex. Schult. F.) (Effect of Temperature and Concentration of Phosphoric Acid (H3PO4) on the Quality of Activated Charcoal of Bambusa blu. Jurnal Penelitian Kehutanan, 62-73.

Variation, T. (2024). Sifat Mutu Arang Aktif Kayu Bidara ( Ziziphus Mauritiana ) Dengan Larutan Kimia Natrium Hidroksida Berdasarkan Variasi Suhu Aktivasi Quality Characteristics of Bidara Wood ( Ziziphus mauritiana ) Activated Temperature Variation Open Access. https://doi.org/10.36761/fagi.v4i2.3583

Wahidin Nuriana, Nurfa Anisa dan Martana. (2013). Karakteristik Biobriket Kulit Durian Sebagai Bahan Bakar Alternatif Terbarukan. Jurnal Teknologi Industri Pertanian, 70-76.

Winata,N.A.S.H., D.R.Lukiwati, dan E.D. Purbajanti. (2014). Peningkatan Produksidan Kualitas Jerami Sorgum Manis Dengan Pemberian Pupuk Organik Dan Fosfat Dari Sumber Yang Berbeda. Jurnal Litbang Provinsi Jawa Tengah, 7-14.

Yustinah, Hartini, dan Zuliani. (2015). Pengaruh Konsentrasi Aktivator Naoh Pada Proses Pembuatan Arang Aktif Terhadap Kualitas Minyak Bekas Setelah Proses Pemurnian . Jurusan Teknik Kimia, 1-7.

Yolanda Simamora, A. C., Yusasrini, N. L. A., & Kencana Putra, I. N. (2021). Pengaruh Jenis Pelarut Terhadap Aktivitas Antioksidan Ekstrak Daun Tenggulun (Protium javanicum Burm. F) Menggunakan Metode Maserasi. Jurnal Ilmu Dan Teknologi Pangan (ITEPA), 10(4), 681. https://doi.org/10.24843/itepa.2021.v10.i04.p13




DOI: https://doi.org/10.31764/protech.v4i1.25068

Refbacks

  • There are currently no refbacks.


Protech Biosystems Journal is indexing in the following databases:

    

 

Editorial Office: